| 特性级别 | 增韧级|||耐低温|||耐老化||| |
| 牌号 | 200-3 |
| 加工级别 | 注堕级||| |
| 品名 | |
| 厂家(产地) | LG-DOW |
| 用途级别 | 通用级|||食品级||| |
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 230℃/3.8kg | ASTM D-1238 | 12 | g/10min |
| 物理性能 | 比重 | ASTM D-792 | 1.04 | g/cm3 | |
| 模具收缩率 | Flow,3.20mm | ASTM D-955 | 0.50-0.80 | % | |
| 机械性能 | 拉伸模量 | ASTM D-638 | 2480 | MPa | |
| 拉伸屈服强度 | ASTM D-638 | 46.9 | MPa | ||
| 拉伸断裂强度 | ASTM D-638 | 35.9 | MPa | ||
| 拉伸屈服伸长率 | ASTM D-638 | 2.0 | % | ||
| 拉伸断裂伸长率 | ASTM D-638 | 18 | % | ||
| 弯曲模量 | 50.0mm Span | ASTM D-790 | 2620 | MPa | |
| 弯曲屈服强度 | 50.0mm Span | ASTM D-790 | 79.3 | MPa | |
| IZOD缺口冲击强度 | 23℃ | ASTM D-256 | 240 | J/m | |
| 热性能 | 热变形温度 | 0.45MPa，未退火，3.20mm | ASTM D-648 | 95.6 | ℃ |
| 热变形温度 | 1.80MPa，未退火，3.20mm | ASTM D-648 | 82.2 | ℃ | |
| 维卡软化温度 | ASTM D-1525 | 98.9 | ℃ | ||
| CLTE | Flow,-40TO40℃ | ASTM E-831 | 0.000088 | cm/cm/℃ | |
| CLTE | Transverse,-40TO40℃ | ASTM E-831 | 0.000085 | cm/cm/℃ | |
| 燃烧性 | 1.52mm | UL 94 | HB | ||